| Pwopriyete | Inite | Metòd tès la | Estanda |
| Dansite lineyè | Tèks | ASTM D1907 | 300±10% |
| Fòs rupture 1) kraze 2) LASE 0.3% 3) LASE0.5% 4) LASE1.0% | N | ASTM D 885 | Min.150 Min.24 Min.40 Min.80 |
| Pwopòsyon | g/cm³ | ASTM D1505 | 2.55±0.05 |
| Modil Young la | Gpa | ASTM D885,D76 | Min.62.5 |
| Elongasyon nan repo | % | ASTM D885 | 1.7-3.0 |
| Vitès absòpsyon | % | Min 150 | |
| Kapasite absòpsyon | % | Min 200 | |
| Kontni imidite | % | Kalite dlo bloke | ≤1 |
| Kalite ki pa bloke dlo | ≤0.5 | ||
| Remak | Absòpsyon sèlman pou kalite dlo bloke | ||
Tan pòs: 22-Sep-2022